Products Code: P.U. Paint/2001     Colour Code

Paint Type   :


Description  :


Usage  :


Unique Properties  :

Two pack anticorrosive polyurethane paint with low solvent content where the hardner used is an aliphatic isocynate 3390 gloss retention hardner.

High hydroxyl functional acrylic co-polymer solution with 3390.

The paint can also be used as atop coat it is suitable for use on steel, zinc, casting and aluminum surface.

P.U. 2001 has excellent resistance to corrosion chemical impact it has high leveling properties and good durability with non yellowing and high level of color and gloss retention.

Pack 1 : Base Paint Polyurethane Paint 2001
Pack 2 : Hardner 3390
Mixing ratio 4 : 1 (v/v)
Gloss Semi Glossy
Thinner Starlite 5001
Method of application By Spray
Hydroxyl value of solid resin, mg. KOH / gm. 120 - 125
Drying Time :
(1) Surface Dry -
(2) Tack Free -
(3)Hard Dry -

35 minutes
1 hours
Over night
Full Cure 7 days
Pot Life : at 30°C (RT) 2½ hrs.
Solids 62 ± 2 by volume
Over Coat After over night
Theoretical spreading rate @ 80 µ D.F.T. 7.75 m2 per liter.


Sr. no. property Test Method Observed Value
1 Thickness per coats SSPC-PA-2 80 microns
2 Dielectric strength ASTM D 149 460 V/mil
3 Hardness shore D ASTM D 2240 95-98
4 Adhesion to steel (pull out test) ASTM D 4541 2900 psi
5 Taber abrasion ASTM D 4060 1260 cycles/ mil
6 Compressive strength ASTM C-109 75 MPa
7 Flexibility NACE RP-0394 0.850